Ι . Descrição do produto
Nossa empresa produz uma folha de titânio Pure Gr1 de alta qualidade, feita de esponja de titânio pura derretida no lingote de titânio e depois enrolada na bobina e sem óleo, com alta pureza de teor de titânio, baixa impurezas, baixo teor de oxigênio, dureza {68-70}}, capacitante e capacitação e não produzirá frutado {68-70}}}} shapes. In the field of aviation, GR1 titanium is widely used in the manufacture of fuselage with its light weight and high strength, which provides a safer and more reliable structural support for the aircraft. In industrial fields such as heat exchangers and desalination plants, GR1 titanium also plays an irreplaceable role, and its excellent corrosion resistance ensures the long-term Operação estável do equipamento .
Ⅱ . Processo de produção
1. rolamento a quente
Produção de lajes: Lajes de titânio, como todos os outros produtos de titânio, originalmente originários de lingotes de titânio ., mas a única diferença é o enorme lingote de titânio, o peso atinge 6 ~ 10 toneladas acima .} O lingot precisa ser forjado para fazer o Billet de Billet 210*1100*8000mm A máquina de moagem é usada para remover a camada oxidada em todos os lados do tarugo) .
Aquecimento: A laje de titânio é colocada na temperatura é alta o suficiente, simplesmente a temperatura certa, a placa de titânio é adequada para a temperatura é de 900 graus ~ 1000 graus . Quando o tempo é longo o suficiente, o tempo geral de aquecimento e retenção é superior a 4 ~ 4 . 5 horas.
Rolamento áspero: After heating the titanium billet by high-pressure water scale removal of surface iron oxide, into the roughing mill for initial forming. Roughing is usually reversible rolling mode (such as two-roll or four-roll mill), through the multi-pass rolling the billet rolling to the middle thickness. This stage may also include spreading or shaping rolling to adjust width and forma .
Acabamento: After the intermediate billet has been cut and tailed, it enters a multi-stand finishing mill (e.g., a seven-stand four-roll mill). Finishing rolling rolls the material to its final thickness through high-speed rolling and precise undercutting control, and adopts closed-loop plate shape control technology to ensure dimensional precisão .
Resfriamento e enrolamento: After finishing, the titanium coils are rapidly cooled down to winding temperature by a laminar flow cooling system, and then wound into coils by a winding machine. Cooling is dynamically adjusted according to different grades of titanium and final rolling temperatures to optimise material properties. The final product may also be subjected to subsequent processing such as bundling and rotulagem .
2. achatamento
Apontamento é o processo de cortar uma bobina ao comprimento exigido pelo cliente para fazer um pedaço de folha antes de ser fornecido ao cliente da fábrica .
Vantagens:
(1) barato e comprimento podem ser decididos livremente;
(2) transporte conveniente, não precisa considerar de acordo com o tamanho da placa de titânio;
(3) conveniente para descarregar, pode ser descarregado de acordo com a necessidade real de tamanho da placa de titânio;
Ⅲ . Detalhes do produto Exibir
Tag: Placa de titânio pura Gr1 de alta qualidade, China de alta qualidade GR1 Fabricantes de placas de titânio puro, fornecedores, fábrica, NIOBIUM Titanium, liga de aço e titânio, Ticl4 H2O, Fornecedores de barras de titânio, Preço da vara de titânio, prata de titânio